Akro-Plastic Akromid® A3 GF 25 (2420) PA 6.6 Conditioned, 25% Glass Filled

Nylon 66, 30% Glass Fiber Filled

Akro-Plastic

产品说明：

AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatures as well as easy processing. AKROMID® A is an engineering plastic compound that allows a broad range of possible applications. On the basis of these standard types, we are able to develop individual compounds for special application needs.

Information from Akro-Plastic

物性信息：

物理性能额定值 (公制)额定值 (英制)测试方法

密度	1.32 g/cc	0.0477 lb/in³	ISO 1183
填料含量	25 %	25 %	ISO 1172
吸水率	2.0 - 2.2 % @Temperature 70.0 °C	2.0 - 2.2 % @Temperature 158 °F	62% r.h., Humidity; ISO 62
饱和吸水率	5.7 - 6.3 % @Time 82800 sec	5.7 - 6.3 % @Time 23.0 hour	ISO 62
线性成型收缩率,Flow	0.0024 cm/cm	0.0024 in/in	ISO 294-4
线性成型收缩率，横向	0.013 cm/cm	0.013 in/in	ISO 294-4

机械性能额定值 (公制)额定值 (英制)测试方法

抗张强度(断裂)	115 MPa	16700 psi	5 [mm/min]; ISO 527-1/2
伸长率 (断裂)	6.5 %	6.5 %	5 [mm/min]; ISO 527-1/2
拉伸模量	6.00 GPa	870 ksi	1[mm/min]; ISO 527-1/2
弯曲强度	200 MPa	29000 psi	2 [mm/min]; ISO 178
弯曲模量	6.20 GPa	899 ksi	2 [mm/min]; ISO 178
简支梁无缺口冲击强度	9.00 J/cm² @Temperature 23.0 °C	42.8 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
简支梁缺口冲击强度	1.30 J/cm² @Temperature 23.0 °C	6.19 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

电气性能额定值 (公制)额定值 (英制)测试方法

体积电阻率	1.00e+10 ohm-cm	1.00e+10 ohm-cm	IEC 60093
表面电阻	1.00e+10 ohm	1.00e+10 ohm	IEC 60093

热性能额定值 (公制)额定值 (英制)测试方法

熔融温度	262 °C	504 °F	ISO 11357-1/3