发布时间:2023-10-13        浏览次数:14        返回列表
PPE日本旭化成300V

Asahi Kasei Xyron® 300V Modified Polyphenylene Ether

Polyphenylene Ether, Heat Resistant

Asahi Kasei

产品说明:

Flame Retardant

Information provided by Asahi Kasei


物性信息:

物理性能额定值 (公制)额定值 (英制)测试方法
比重1.08 g/cc1.08 g/cc23°C; ASTM D792
水分吸收0.100 %0.100 %23°C, 50% RH 24 hours; ASTM D570
线性成型收缩率0.0050 - 0.0070 cm/cm0.0050 - 0.0070 in/inASTM D955
机械性能额定值 (公制)额定值 (英制)测试方法
抗张强度(屈服)44.0 MPa6380 psi23°C, 50% RH; ASTM D638
伸长率 (断裂)50 %50 %23°C, 50% RH; ASTM D638
弯曲强度70.0 MPa10200 psi23°C, 50% RH; ASTM D790
弯曲模量2.35 GPa341 ksi23°C, 50% RH; ASTM D790
悬壁梁缺口冲击强度1.76 J/cm

@Thickness 6.40 mm, Temperature 23.0 °C

3.30 ft-lb/in

@Thickness 0.252 in, Temperature 73.4 °F

ASTM D256

2.30 J/cm

@Thickness 3.20 mm, Temperature 23.0 °C

4.31 ft-lb/in

@Thickness 0.126 in, Temperature 73.4 °F

ASTM D256
电气性能额定值 (公制)额定值 (英制)测试方法
体积电阻率1.00e+16 ohm-cm1.00e+16 ohm-cm50% RH; ASTM D257
表面电阻1.00e+16 ohm1.00e+16 ohm50% RH; ASTM D257
介电常数2.9

@Frequency 1e+6 Hz

2.9

@Frequency 1e+6 Hz

50% RH; ASTM D150

2.9

@Frequency 1e+6 Hz

2.9

@Frequency 1e+6 Hz

50% RH; ASTM D150
介电强度25.0 kV/mm

@Thickness 2.00 mm

635 kV/in

@Thickness 0.0787 in

Short time; ASTM D149
耗散因数0.0030

@Frequency 60 Hz

0.0030

@Frequency 60 Hz

50% RH; ASTM D150

0.0040

@Frequency 1e+6 Hz

0.0040

@Frequency 1e+6 Hz

50% RH; ASTM D150
耐电弧性70 sec70 secTungsten; ASTM D495
热性能额定值 (公制)额定值 (英制)测试方法
线性热膨胀系数75.0 µm/m-°C

@Temperature -30.0 - 60.0 °C

41.7 µin/in-°F

@Temperature -22.0 - 140 °F

ASTM D696
载荷下热变形温度(1.8 MPa)100 °C212 °FASTM D648
可燃性(UL94)V-1

@Thickness 1.60 mm

V-1

@Thickness 0.0630 in



V-1

@Thickness 3.20 mm

V-1

@Thickness 0.126 in


加工性能额定值 (公制)额定值 (英制)测试方法
加工温度°C°FResin Temperature
模具温度50.0 - 80.0 °C°F
干燥温度90.0 - 100 °C°FPre-drying Temperature
干燥时间2 - 4 hour2 - 4 hour


核心提示:PPE,日本旭化成,300V,PPE日本旭化成,日本旭化成300V