500R-739
聚碳酸酯#防弹胶|PC
沙伯基础（原GE）
填充物:玻纤增强
外观:黑色
物性信息：
| 吸水率 | 0.12 | % | ASTM D-570 |
| 阻燃性 | UL 94 | ||
| 5V | |||
| 3.0 | mm | ||
| 比重 | 1.25 | ASTM D--792 | |
| 模具收缩率 (3.2mm) | 2-4 | 10-3 | ASTM D-955 |
| 阻燃性 | 1.5 | mm | UL 94 |
| 增强 | 10 | % | |
| 阻燃性 | V-0 | UL 94 |
| 缺口冲击强度 (23℃) | 107 | J/m | ASTM D-256 |
| 断裂伸长率 | 15 | % | ASTM D-638 |
| 拉伸强度 | |||
| 66 | MPa | ASTM D-638 | |
| 55 | MPa | ASTM D638 | |
| 洛氏硬度 | 124 | ASTM D-785 | |
| 弯曲模量 | 3445 | MPa | ASTM D-790 |
| 弯曲强度 | 103 | MPa | ASTM D-790 |
| 损耗因数 (1MHz) | 0.0075 | ASTM D-150 | |
| 介电常数 (1MHz) | 3.05 | ASTM D-150 | |
| 损耗因数 (60Hz) | 0.0008 | ASTM D-150 | |
| 体积电阻率 | 1.0×10 | Ω.cm | ASTM D-257 |
| 介电常数 (60Hz) | 3.1 | ASTM D-150 |
| 热变形温度 (0.45MPa) | 146 | ℃ | ASTM D-648 |