产品说明：
Homopolymer Polypropylene, 30% Talc Reinforced, 10 Melt Flow
物性信息：
| 填料/增强材料 |
|
| 特性 |
|
| RoHS 合规性 |
|
| 形式 |
|
| 比重 | 1.15 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| 抗张强度 (屈服, 23°C) | 32.8 | MPa | ASTM D638 |
| 伸长率 | ASTM D638 | ||
| 屈服, 23°C | 5.0 | % | ASTM D638 |
| 断裂, 23°C | 14 | % | ASTM D638 |
| 弯曲模量 - 正切 (23°C) | 2410 | MPa | ASTM D790 |
| 弯曲强度 (23°C) | 48.3 | MPa | ASTM D790 |
| 悬壁梁缺口冲击强度 (23°C, 3.18 mm) | 27 | J/m | ASTM D256 |
| 载荷下热变形温度 (0.45 MPa, 未退火) | 132 | °C | ASTM D648 |