Acrylonitrile Butadiene Styrene + Nylon
INEOS Styrolution Group GmbH
产品说明：
Triax 1120 resin is an ABS (Acrylonitrile Butadiene Styrene)/Nylon 6 alloy for injection molding. It is a semicrystalline thermoplastic with excellent processibility, good chemical resistance, good fatigue performance, and excellent abrasion characteristics. Triax 1120 resin exhibits a good balance of impact strength and flow properties.
Typical applications include housings, shrouds and handles for components of lawn and garden equipment, power tools, appliances, and sporting goods. Automotive applications include fasteners and interior functional components, housings, and shrouds. As with any product, use of Triax 1120 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
物性信息：
基本信息黄卡编号
E44741-235663
特性半结晶
抗撞击性，良好
可加工性，良好
良好的流动性
良好耐磨损性
耐化学性良好
耐疲劳性能
用途把手
草坪和园林设备
动力/其它工具
家电部件
紧固件
汽车领域的应用
体育用品
外壳
机构评级EC 1907/2006 (REACH)
形式粒子
加工方法注射成型
多点数据Isochronous Stress vs. Strain (ISO 11403-1)
Isothermal Stress vs. Strain (ISO 11403-1)
Secant Modulus vs. Strain (ISO 11403-1)
Shear Modulus vs. Temperature (ISO 11403-1)
Viscosity vs. Shear Rate (ISO 11403-2)
物理性能干燥调节后的单位制测试方法比重1.061.06g/cm³ASTM D792特定体积0.9400.940cm³/gASTM D792收缩率 - 流动1.01.0%ASTM D955吸水率ASTM D570 23°C, 24 hr1.11.1%ASTM D570 饱和, 23°C4.34.3%ASTM D570硬度干燥调节后的单位制测试方法洛氏硬度 (R 级)10590
ASTM D785机械性能干燥调节后的单位制测试方法拉伸模量2030--MPaASTM D638抗张强度 (屈服)43.440.0MPaASTM D638伸长率 (断裂)140290%ASTM D638弯曲模量20701170MPaASTM D790弯曲强度 (屈服)75.256.9MPaASTM D790冲击性能干燥调节后的单位制测试方法悬壁梁缺口冲击强度
ASTM D256 -40°C, 3.18 mm8080J/mASTM D256 -40°C, 6.35 mm6975J/mASTM D256 23°C, 3.18 mm800800J/mASTM D256 23°C, 6.35 mm750750J/mASTM D256装有测量仪表的落镖冲击
ASTM D3763 -40°C, 2.54 mm, Total Energy47.559.7JASTM D3763 23°C, 2.54 mm, Total Energy42.048.8JASTM D3763热性能干燥调节后的单位制测试方法载荷下热变形温度
ASTM D648 0.45 MPa, 未退火, 3.18 mm90.087.8°CASTM D648 0.45 MPa, 未退火, 6.35 mm97.296.1°CASTM D648 1.8 MPa, 未退火, 3.18 mm65.062.2°CASTM D648 1.8 MPa, 未退火, 6.35 mm73.972.2°CASTM D648维卡软化温度197170°CASTM D1525 1线形热膨胀系数 - 流动
ASTM D696 -40 到 22°C9.9E-51.1E-4cm/cm/°CASTM D696 22 到 83°C1.5E-41.4E-4cm/cm/°CASTM D696RTI Elec (1.57 mm)110110°CUL 746RTI Imp (1.57 mm)65.065.0°CUL 746RTI (1.57 mm)105105°CUL 746电气性能干燥调节后的单位制测试方法表面电阻率8.3E+153.2E+13ohmsASTM D257体积电阻率 29.7E+159.0E+12ohms·cmASTM D257介电强度 3(23°C, 1.57 mm, in Oil)1715kV/mmASTM D149介电常数 4(1 MHz)3.503.50
ASTM D150耗散因数 5(1 MHz)0.0240.039
ASTM D150可燃性干燥调节后的单位制测试方法UL 阻燃等级
UL 94 1.57 mmHBHB
UL 94 3.18 mmHBHB
UL 94光学性能干燥调节后的
测试方法Gardner光泽度
ASTM D523 20°7878
ASTM D523 60°9191
ASTM D523注射干燥单位制
干燥温度87.8°C
干燥时间2.0 到 4.0hr
建议的最大水分含量0.15 到 0.35%
建议注射量50 到 70%
建议的最大回制料比例20%
料筒后部温度232 到 266°C
料筒中部温度232 到 266°C
料筒前部温度232 到 266°C
射嘴温度249 到 260°C
加工（熔体）温度238 到 271°C
模具温度37.8 到 65.6°C
注塑压力41.4 到 82.7MPa
注射速度快速
背压0.345 到 0.689MPa
锁模力4.1 到 6.9kN/cm²
垫层< 3.18mm
螺杆长径比20.0:1.0