HW610HT
丙烯腈/乙烯/苯乙烯共聚物#|AES
锦湖日丽
产品用途:后视镜外壳、支架、车门饰件、拢流罩/雨水槽，空调室外部件道路标牌，摩托车，自行车零件，摩托艇，帆船零件，滑雪板，电秤车，广告标牌。
填充物:通用
外观:黑
物性信息：
| 密度 (23℃) | 1.04 | g/cm | ASTM D-792 |
| 熔体流动速率 | ASTM D-1238 | ||
| (220℃×10kg) | 12 | g/10min | |
| (200℃×5kg) | 1.5 | g/10min |
| 阻燃性 | HB | CLASS | UL 94 |
| 光泽度 (60℃) | 88 | ASTM D-523 |
| IZOD缺口冲击强度 (23℃.3.2mm) | 11 | kg.cm/cm | ASTM D-256 |
| 拉伸强度 (50mm/min) | 550 | Kg/cm | ASTM D-638 |
| 伸长率 (50mm/min) | 25 | % | ASTM D-638 |
| 弯曲强度 (3mm/min) | 700 | Kg/cm | ASTM D-790 |
| IZOD缺口冲击强度 (23℃.6.4mm) | 10 | kg.cm/cm | ASTM D-256 |
| 弯曲模量 (3mm/min) | 24000 | Kg/cm | ASTM D-790 |
| 洛氏硬度 (R scale) | 106 | R | ASTM D-785 |
| 成型收缩率 | 0.4-0.7 | % | ASTM D-955 |
| 热变形温度 (1/4"(18.6kg/cm)) | 97(207) | ℃(℉) | ASTM D-648 |